Features

CIP (Rubber Press) Products are highly and homogeneously condensed non-porous products because they are made under the ultra-high pressure in all the directions.
Rubber molds, which are suitable for smaller quantity production but less expensive, are used in the CIP manufacturing process.

Zirconia Crushing roller (upper)・Stirring blade (lower left)・Crushing blade (lower right)
Zirconia Crushing roller (upper)・Stirring blade (lower left)・Crushing blade (lower right)
Zirconia CIP product (special shape)
Zirconia CIP product (special shape)
Zirconia Crushing blade (left) and Stirring blade (right)
Zirconia Crushing blade (left) and Stirring blade (right)
Yttria-stabilized zirconia CIP molded product
Yttria-stabilized zirconia CIP molded product

Product group : FZ-PSY

  • Ceramics with high level of intensity and fracture toughness
  • The most popular materials for wear resistant or shock resistant parts

Product group : FZ-PS8Y

  • Having unique features which differs from that of alumina in response to metals

Table of Physical Properties FZ-PSY Series

Product group FZ-PS3Y FZ-PS8Y
Materials Partially Stabilized Zirconia Fully Stabilized Zirconia
Appearance Non-porous
Chemical Ingredients
(Wｔ%)		 ZrO2 94 86
Y2O3 5.5 (3mol) 14.0 (8mol)
Aｌ2O3 0.2 0.0
Specific Gravity
(g/cm3) 		6.0 5.8
Water-absorption Rate
(%) 		0.0 0.0
Thermal Conductivity
(W/mk) 		3 8
Flexural Strength
(MPa) 		1200 300
Normal operating temperature
(℃) 		1000 1400
Impedance
(20℃,Ωcm) 		1010～13 –
Thermal Shock Resistance
(℃/hr) 		300 –
Color Appearance Milky White
Intended Application Wear resistant parts(Nozzle, Ring and Bearing)
Parts with characteristic feature of high-intensity and fracture-toughness
Zirconia pot mills
Screw / Stirring blades		 Jigs for sintering electronic parts(Corrosion resistant setter) Thermal insulation materials
※ Note that the features listed above are reference values and are not guaranteed.